Dhulka dhif ah os os oxide ytrium ok okside budo 1314-36-9
Yttrium oxide Horudhac kooban
Qaaciddada (y2O3)
Cas Maya.: 1314-36-9
Daahirnimo: 99.999%
SSA: 25-45 m2 / g
Midab: Caddaan
Morphology: lafdhabarta
Cufnaanta badan: 0.31 g / cm3
Cufnaanta dhabta ah: 5.01 g / cm3
Miisaanka Moleculal: 225.81
Barta dhalaalaysa: 2425 heerka Celsium
Muuqaalka: budada cad
Xabfaynta
Deganaansho: waxyar hygroscopic
Codsiyada oxide ee ytrium
1: ytrierna oxide, oo sidoo kale loo yaqaan yttria, oo sidoo kale yaantooniska 'yttria' waa qalabka ugu muhiimsan ee loo yaqaan 'tri-banches' oo ah midhaha xargaha dhulka oo siiya midabka casaanka ee tuubooyinka TV-ga & tuubooyinka kombiyuutarka.
2: Warshadaha indhaha, ytririum oxide waxaa loo isticmaalaa in lagu soo saaro yttrium-bir-garyin, kuwaas oo ah kuwa waxtarka leh ee mikrowave-ka waxtarka badan.
3: Daahirsanaanta hoose ee ytririum oxide waxaa si balaadhan loogu dabaqayaa majaajillada elektiroonigga ah. Waxaa si weyn loo isticmaalaa in lagu sameeyo EU: YVO4 iyo EU: Y2O3 POLO3 POSHESHORS oo siiya midabka casaanka tuubooyinka sawirka midabka midabka leh.
4: ytrium oxide waxaa sidoo kale loo isticmaalaa in lagu sameeyo yttrium-bir-garyin, kuwaas oo ah kuwa waxtarka leh ee miraha microwave-ka ee waxtarka leh.
| Wax | Faahfaahinta | Natiijooyinka Tijaabada | ||||||
| Y2O3 / Treo (%, min) | 99.995 | 99.999 | ||||||
| Treo (%, min) | 98 | 98.38 | ||||||
| Cabbirka walxaha | 30-60nm, 1.0-2.00.0um, 0.3-0.6um, 0.6-10.6 | Is waafajin | ||||||
| Reebitaanka (/ Reo,%) | ||||||||
| La2o3 | ≤0.0005 | ≤0.0001 | ||||||
| COO2 | ≤0.0005 | ≤0.0001 | ||||||
| Pr6O11 | ≤0.0002 | ≤0.0001 | ||||||
| Nd2o3 | ≤0.0002 | ≤0.0001 | ||||||
| Sm2o3 | ≤0.0002 | ≤0.0001 | ||||||
| EU2O3 | ≤0.0002 | ≤0.0001 | ||||||
| GD2O3 | ≤0.0002 | ≤0.0001 | ||||||
| TB4O7 | ≤0.0002 | ≤0.0001 | ||||||
| Dy2O3 | ≤0.0002 | ≤0.0001 | ||||||
| Ho2o3 | ≤0.001 | ≤0.0001 | ||||||
| Er2O3 | ≤0.001 | ≤0.0001 | ||||||
| Tm2o3 | ≤0.0001 | ≤0.00002 | ||||||
| Yb2o3 | ≤0.0001 | ≤0.00002 | ||||||
| Lu2O3 | ≤0.0001 | ≤0.00002 | ||||||
| Loi | ≤2% | |||||||